National Standard 90kg Liquid Ammonia Steel Welding Refillable Gas Cylinder
|FOB Price:||US $300 / Piece|
|Min. Order:||50 Pieces|
|Min. Order||FOB Price|
|50 Pieces||US $300/ Piece|
|Payment Terms:||T/T, Western Union|
- Model NO.: HJL350-100-3S
- Application: Liquefied Gas
- Pressure: 1.6MPa≤p<10.0MPa
- Pressure Level: Medium Pressure (1.6MPa≤p<10.0MPa)
- Total Length: 1380mm
- Body Thickness: 6mm
- Colour: Black
- Specification: 100
- HS Code: 73110090
- Function: Storage Pressure Vessel
- Material: HP345 GB6653
- Storage Medium: Liquid Chlorine
- Condition: New
- Body Diameter: 350mm
- Life: 12 Years
- Trademark: lanyi
- Origin: China
GN5100-2011 standard responsible for drafting unit,welding gas cylinder production and sales of the national
market more than 45%, and 90% for export welding gas cylinder design, manufacturing. Five types of welding
gas cylinder has nine times by the national,provincial an ministry as high quality products, the products are ex-
ported to the west Asia, the middle east,western Europe,southeast Asia,Japan,Korea,Germany, the United stat-
es and other countries and regions, for the domestic welding gas cylinder's biggest export enterprise. In october
2001 by the Chinese entrepreneurs assosiation awarded the "welding gas cylinder head of the national industry"
1 The cylinder should be manufactured,inspected and accepted according to GB5100 welded /steel/gas cylinder
2 The longitdinal and circumferential seams must be welded automaticly by electric-arc welding ,the tensile strengthof joints must be not less than minimum value required.
3 The longitdinal and circumferential welds welds must be examined by ≥20% X-ray radiagraphy.
4 The cylinder must be subjected to heat treatment to relieve stress entirely after all welding
operation have been completed.
5 The cylinder must withstand a hydrostatic test to 45bar without leakage and deform after
heat treatment. Dry the internal surface after testing.
6 The cylinder must withstand a pneumatic test to 15bar with leakage after hydrostatic test.
7 Internal surface must be subjected to rust cleaning before assembly an external surface
must be subjected to shot blasting after assembly.The cylinder must be coated with anti-
corrosion primer and yellow finish paint.
8 Tread seal should be winded with PTFE.
9 HP295 can be used as material of body (ends and shell) .
|nominal working pressure kgf/cm2||10|
|hydrostatic test pressure kgf/cm2||15|
|operating temperature (ºC)||-40~60|
|naminal water capacity (L)||100|
|maximum permissble filling weght (kg)||60|
|corrosion allowance (mm)||1|
|yield temperature of fusible plug (ºC)||70+5|